Products |
|
White Group -
Mugla White |
 |
|
PHYSICO-MECHANICAL SPECIFICATIONS |
|
Hardness |
(Mohs) |
3 |
|
Unit Volume by Weight |
(gr/cm
3 ) |
2,69 |
|
Density |
(gr/cm
3 ) |
2,71 |
|
Water Absorption at Atmospheric
Pressure |
By Weight(%0) |
0,2 |
|
|
By Volume (%0) |
0,5 |
|
Water Absorption at Boiling Water
|
By Weight(%0) |
0,2 |
|
|
By Volume (%0) |
0,5 |
|
Porosity |
(%0) |
0,5 |
|
Compressive Strength |
(Kgf/cm
2 ) |
600 |
|
Compressive Strength After Freezing
|
(Kgf/cm
2 ) |
500 |
|
Strength to Blow |
(Kgf/cm
2 ) |
6 |
|
Strength to Bending |
(Kgf/cm
2 ) |
70 |
|
Modules of Elasticity |
(Kgf/cm
2 ) |
53,63x10^4 |
|
Ratio of Fullness |
(%0) |
99,3 |
|
Degree of Pores |
(%0) |
0,7 |
|
Average Abrasion Strength
|
(cm
3
/50cm
2
) |
32,36 |
|
Average Tensile Strength,
|
(Kgf/cm
2 ) |
509,86 |
|
CHEMICAL ANALYSIS |
% |
|
SiO2 |
0,1 |
|
Fe2O3 |
0,1 |
|
CaO |
55,5 |
|
MgO |
0,2 |
|
|
|
|
 |
)